>> Structure cristallographique et propriétés
physiques des matériaux
|
|
Grandeur
|
Masse
volumique
|
Température
de fusion
|
Coefficient
de Dilatation
|
Capacité
calorifique
|
| METAUX |
|
| Aluminium |
2.698
|
660.2
|
24
|
900
|
| Argent |
10.50
|
960.8
|
19
|
235
|
| Béryllium |
1.846
|
1278
|
12
|
2422
|
| Cadmium |
8.647
|
321
|
29
|
230
|
| Chrome |
7.194
|
1890
|
8.2
|
455
|
| Cobalt |
8.8
|
1495
|
12.1
|
418
|
| Cuivre |
8.932
|
1083
|
16.4
|
386
|
| Etain |
5.765
|
231.9
|
23
|
|
| Fer |
7.873
|
153.5
|
11.8
|
448
|
| lithium |
0.533
|
179
|
56
|
2980
|
| Magnésium |
1.737
|
651
|
26
|
1012
|
| Manganèse |
7.473
|
1244
|
23
|
|
| Molybdène |
4.508
|
2610
|
4.9
|
247
|
| Nickel |
8.907
|
1453
|
13
|
443
|
| Niobium |
8.578
|
2468
|
7.2
|
|
| Or |
19.281
|
1063
|
14
|
130
|
| Platine |
21.47
|
1769
|
11.7
|
132
|
| Plomb |
11.341
|
327.5
|
29
|
1.42
|
| Tantale |
16.47
|
2996
|
605
|
|
| Titane |
4.508
|
1675
|
8.8
|
524
|
| Tungstène |
19.253
|
3410
|
4.4
|
142
|
| Vanadium |
6.09
|
1890
|
|
|
| Zinc |
7.0134
|
419.4
|
31.2
|
388
|
| Zirconium |
6.507
|
1852
|
6.3
|
316
|
| |
|
|
|
|
| COVALENTS |
|
| Carbone C diam |
3.516
|
>3500
|
1.2
|
510
|
| Silicium |
2.329
|
1410
|
7.63
|
879
|
| Carbure Si SiC |
3.22
|
2300
|
4.7
|
|
| |
|
|
|
|
| OXYDES |
|
| Alumine |
3.9
|
2050
|
8.8
|
775
|
| Silice |
2.6
|
|
0.5
|
740
|
| Oxyde de calcium |
|
2580
|
|
|
| Magnésie |
3.5
|
2850
|
113.5
|
940
|
| Nutile |
|
1630-1850
|
|
|
| |
|
|
|
|
| POLYMERES |
|
| Polyéthylène basse densité |
0.92
|
98-115
|
100-220
|
2200
|
| Haute densité |
0.95
|
130-137
|
60-110
|
2100
|
| Polychlorure de Vynil |
1.4
|
160
|
50-100
|
|
| polystyrène |
1.04
|
74-105
|
50-83
|
1360
|
| PMMA |
1.18
|
85-105
|
50-90
|
1500
|
| Epoxy |
1.3
|
370-390
|
55-90
|
1800
|
|
 |
![]() |
|
|